硬度对照表
发布日期：2012-08-29 兰生客服中心 浏览：6055
分享到：
根据德国标准DIN50150,以下是常用范围的钢材抗拉强度与维氏硬度、布氏硬度、洛氏硬度的对照表。
抗拉强度
Rm
N/mm2
| 维氏硬度
HV
| 布氏硬度
HB
| 洛氏硬度
HRC
|
250
| 80
| 76.0
| -
|
270
| 85
| 80.7
| -
|
285
| 90
| 85.2
| -
|
305
| 95
| 90.2
| -
|
320
| 100
| 95.0
| -
|
335
| 105
| 99.8
| -
|
350
| 110
| 105
| -
|
370
| 115
| 109
| -
|
380
| 120
| 114
| -
|
400
| 125
| 119
| -
|
415
| 130
| 124
| -
|
430
| 135
| 128
| -
|
450
| 140
| 133
| -
|
465
| 145
| 138
| -
|
480
| 150
| 143
| -
|
490
| 155
| 147
| -
|
510
| 160
| 152
| -
|
530
| 165
| 156
| -
|
545
| 170
| 162
| -
|
560
| 175
| 166
| -
|
575
| 180
| 171
| -
|
595
| 185
| 176
| -
|
610
| 190
| 181
| -
|
625
| 195
| 185
| -
|
640
| 200
| 190
| -
|
660
| 205
| 195
| -
|
675
| 210
| 199
| -
|
690
| 215
| 204
| -
|
705
| 220
| 209
| -
|
720
| 225
| 214
| -
|
740
| 230
| 219
| -
|
755
| 235
| 223
| -
|
770
| 240
| 228
| 20.3
|
785
| 245
| 233
| 21.3
|
800
| 250
| 238
| 22.2
|
820
| 255
| 242
| 23.1
|
835
| 260
| 247
| 24.0
|
850
| 265
| 252
| 24.8
|
865
| 270
| 257
| 25.6
|
880
| 275
| 261
| 26.4
|
900
| 280
| 266
| 27.1
|
915
| 285
| 271
| 27.8
|
930
| 290
| 276
| 28.5
|
950
| 295
| 280
| 29.2
|
965
| 300
| 285
| 29.8
|
995
| 310
| 295
| 31.0
|
1030
| 320
| 304
| 32.2
|
1060
| 330
| 314
| 33.3
|
1095
| 340
| 323
| 34.4
|
1125
| 350
| 333
| 35.5
|
1115
| 360
| 342
| 36.6
|
1190
| 370
| 352
| 37.7
|
1220
| 380
| 361
| 38.8
|
1255
| 390
| 371
| 39.8
|
1290
| 400
| 380
| 40.8
|
1320
| 410
| 390
| 41.8
|
1350
| 420
| 399
| 42.7
|
1385
| 430
| 409
| 43.6
|
1420
| 440
| 418
| 44.5
|
1455
| 450
| 428
| 45.3
|
1485
| 460
| 437
| 46.1
|
1520
| 470
| 447
| 46.9
|
1555
| 480
| (456)
| 47.7
|
1595
| 490
| (466)
| 48.4
|
1630
| 500
| (475)
| 49.1
|
1665
| 510
| (485)
| 49.8
|
1700
| 520
| (494)
| 50.5
|
1740
| 530
| (504)
| 51.1
|
1775
| 540
| (513)
| 51.7
|
1810
| 550
| (523)
| 52.3
|
1845
| 560
| (532)
| 53.0
|
1880
| 570
| (542)
| 53.6
|
1920
| 580
| (551)
| 54.1
|
1955
| 590
| (561)
| 54.7
|
1995
| 600
| (570)
| 55.2
|
2030
| 610
| (580)
| 55.7
|
2070
| 620
| (589)
| 56.3
|
2105
| 630
| (599)
| 56.8
|
2145
| 640
| (608)
| 57.3
|
2180
| 650
| (618)
| 57.8
|
| 660
|
| 58.3
|
| 670
|
| 58.8
|
| 680
|
| 59.2
|
| 690
|
| 59.7
|
| 700
|
| 60.1
|
| 720
|
| 61.0
|
| 740
|
| 61.8
|
| 760
|
| 62.5
|
| 780
|
| 63.3
|
| 800
|
| 64.0
|
| 820
|
| 64.7
|
| 840
|
| 65.3
|
| 860
|
| 65.9
|
| 880
|
| 66.4
|
| 900
|
| 67.0
|
| 920
|
| 67.5
|
| 940
|
| 68.0 |
硬度试验是机械性能试验中最简单易行的一种试验方法。为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。
实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
下面是本站根据由实验得到的经验公式制作的快速计算器，有一定的实用价值，但在要求数据比较精确时，仍需要通过试验测得。
|
|
|